You would never get the same properties in welding rods.
Don't forget the head would need to be heated to a given temp evenly then welded then carefully allowed to cool evenly to avoid cracking as the head and alloy filler rod will cool at different rates.

Good as a water jacket repair. But just think about that pic if one of those valve seats fall out......

Anyway back to the original op's question.