Originally Posted by
flannigan
Ok I feel as though I'm wasting my time explaining this to you but here goes
Any fucking idiot can see with there own eyes that the pistons have melted !
When metal gets hot it expands !
This would be when the piston being alli and the bore being steel was when the piston locked in the bore !
So can you not accept the facts or still trying to bullshit you're way out of it I suppose if you continue talking shit you're whole life then you may start believing you're own shit
Originally Posted by
botters
fucks sake danny you are clutching at straws now as james has just pointed out above, admit defeat pay for the pistons and see if you can get back some respect by doing so
What the fuck are you on about ??
the pistons have clearly seen det in their life but when can t be said!!
The melted part is down to heat and the bores gripping them thats for sure and thats when the cracks appeared!!! this did not happen because of det!!!
Its hard work on here with so many haters and so many people who dont know what they are looking at..
When a piston badly dets then temps will sore but that isnt bad det and didnt contribute to high temps gripping the pistons!!!
Did no one listen to what karl norris had to say???
Is he talking shit to??
cheers danny