get it hot to around 200-250 degrees and weld it immediatley then put back in the oven and bring heat down ten degrees every 5 minutes or so until cool or leave to cool by covering it completley in sand, mig welding is fine if done this way but you have to be aware that while cooling it can still crack, usually accompanied by a loud bang lol!