no i would not mig it ,its not good enough ,but it could be tig welded which would be much better you would need to clean it with solvent so there is no oil contamination & if you can grind into the crack so the weld can get in as far as possible so it will be a good strong weld .or you could use a dye grinder to get into the crack then you can drill the hole & re tap it .